Specification |
File Format: STL;
Application: Auto and Motorcycle Accessory, Household Appliances, Furniture, Hardware, Machinery Accessory;
Printer Material: Nylon;
Nozzle Number: None;
Forming Technology: SLS;
CNC Machining or Not: Not CNC Machining;
Keyword: Laser Machining, Rapid Prototyping;
Color: White, Black, Yellow, Other Colors Can Be Painted;
Shipment: DHL EMS TNT UPS;
Material Capabilities: Nylon;
Feature: Durable;
MOQ: 1 Piece;
Lead Time: 2-5 Days;
Type: Other Machining Services, Rapid Prototyping;
Packing: Carton Box;
Micro Machining or Not: Not Micro Machining;
|
File Format: Standard;
Printer Material: Standard;
Nozzle Number: Standard;
Forming Technology: Standard;
Sku: 11b138;
MOQ: 5;
Delivery Time: 7days;
Support Customization: Yes;
|
File Format: STEP;
Application: Auto and Motorcycle Accessory, Household Appliances, Furniture, Hardware, Machinery Accessory, Aerospace Industry;
Printer Material: Metal;
Nozzle Number: 4;
Forming Technology: 3DP;
Heat Deflection: 88-89;
Glass Transition Temperature: 105;
Vicat Softening Temperature: 100;
Coefficient of Thermal Expansion: 120;
Thermal Conductivity (W/M.K)): 0.1;
Specific Heat Capacity(J/Kg.K): 900;
Tensile Strength MPa: 42.5-44.8;
Modulus of Elasticity(Gpa): 2.0-2.6;
Flexural Strenght(MPa): 60.6-73.1;
Flexural Modulus(Gpa)): 2.25-2.28;
|
File Format: STEP;
Application: Auto and Motorcycle Accessory, Household Appliances, Furniture, Hardware, Machinery Accessory, Aerospace Industry;
Printer Material: Metal;
Nozzle Number: 4;
Forming Technology: 3DP;
Heat Deflection: 88-89;
Glass Transition Temperature: 105;
Vicat Softening Temperature: 100;
Coefficient of Thermal Expansion: 120;
Thermal Conductivity (W/M.K)): 0.1;
Specific Heat Capacity(J/Kg.K): 900;
Tensile Strength MPa: 42.5-44.8;
Modulus of Elasticity(Gpa): 2.0-2.6;
Flexural Strenght(MPa): 60.6-73.1;
Flexural Modulus(Gpa)): 2.25-2.28;
|
File Format: STEP;
Application: Auto and Motorcycle Accessory, Household Appliances, Furniture, Hardware, Machinery Accessory, Aerospace Industry;
Printer Material: Metal;
Nozzle Number: 4;
Forming Technology: 3DP;
Heat Deflection: 88-89;
Glass Transition Temperature: 105;
Vicat Softening Temperature: 100;
Coefficient of Thermal Expansion: 120;
Thermal Conductivity (W/M.K)): 0.1;
Specific Heat Capacity(J/Kg.K): 900;
Tensile Strength MPa: 42.5-44.8;
Modulus of Elasticity(Gpa): 2.0-2.6;
Flexural Strenght(MPa): 60.6-73.1;
Flexural Modulus(Gpa)): 2.25-2.28;
|