| Specification |
Classification: Corundum Brick;
Feature: High-Temperature Resistant;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Raw Material: Bauxite;
Alumina Content: 70%;
|
Classification: Clay, Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method, Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Sio2: 15%~45%;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Roll, Ceramic Fiber Blanket;
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃, 1430;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1360/1430;
Certifiacte: ISO9001, CE, etc;
Working Temperature: 1050-1350;
Bulk Density(g/cm3): 96-160;
Linear Shrinkage After Heating: -3;
Thermal Conductivity: 0.09-0.76;
Al2O3: 34-52;
Al2O3+Sio2: 96-99;
Tensile Strength: 0.05-0.06;
|
Feature: High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3 Content (%): >42%;
Apparent Porosity/%: 10%~18%;
Bulk Density(g/cm3): 2.0-2.5g/cm3;
Refractoriness (Degree): Common (1580°< Refractoriness< 1770°);
Size: Customized Size;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 42~45%;
Apparent Porosity: 10%~18%;
C.C.S: 48~70MPa;
Bulk Density: 2.25-2.4G/Cm3;
Refractoriness: 1750c;
|