Specification |
Material: PVC;
Applications: Transportation Textiles;
Type: Tarpaulin;
Style: PVC Coated;
Pattern: Plain;
Width: 1.5-3m;
Gram Weight: 1500GSM;
Structure: Fabric Form;
Brand: Livite;
Colour: Customized;
Base Fabric: 100% Polyester;
Coating Material: PVC;
Thickness: 0.9mm;
Tensile Strength W/F: 4000/3700 N/5cm;
Tear Resistance W/F: 750/650 N;
Welding Adhesion: 150 N/5 Cm;
Temperature Resistance: -30 to 70 Degree;
Surface Finish: Double-Side Acrylic;
Application: Roll Door Tarpaulin;
|
Material: 100% Polyester;
Applications: Bags, Covers;
Type: Tarpaulin;
Style: PVC Laminated;
Pattern: Plain;
Width: 58/60";
Gram Weight: 610GSM;
Structure: Yarn Form;
Color: According to Ral/Pantone Color Chart;
Feature: Waterproof, Fire Proof, UV-Resistance...;
Application: Trucks, Tents, and Other Different Cover;
Process Type: Laminate and Coat;
|
Material: 100% Cotton;
Applications: Architectural Textiles;
Type: Dryer Fabric;
Style: Dyed;
Pattern: Plain;
Width: 58"-110";
Gram Weight: 185GSM;
Structure: Yarn Form;
Advantage: Smooth, No Allergy, Non-Toxic;
Roll Length: Depend on Your Request;
OEM: Available;
Supply Ability: 1200 Ton/Tons Per Month;
Loading Quantity: One 20'gp Can Load About 5 Tons One 40'hq Can Load;
|
Material: PVC65% PVC, 35% Polyester;
Applications: Agriculture Textiles;
Type: Tarpaulin;
Style: PVC Laminated;
Pattern: Plain;
Width: 1.02~3.2m;
Gram Weight: 610g;
Structure: Yarn Form;
Color: White/Blue/Red/Yellow/Green/Grey, Any Color You Ne;
Standard: DIN/GB/ISO//ANSI;
Process: Lamianted and Coated;
Thread: 200X300d/ 500X300d/500X500d/1000X1000d/1500X1500d;
Density: 18X12, 12X18, 9X9, 18X18, 20X20, 30X30;
Weight: 240g, 260g, 280g, 300g, 340g, 380g, 400g, 440g, 5;
Finish: Glossy & Matt;
Length: 30m, 50m, 70m, 100m;
Package: Water Proof Kraft Paper/Hard Tube with Print Your;
|
Material: 100% Polyester;
Applications: Security Textiles;
Type: Dwf;
Style: PVC Coated;
Pattern: Plain;
Width: up to 2.1m;
Structure: Fabric Form;
Color: Customized;
Thickness: up to 2mm;
Trade Mark: Yatai;
Fire Retardant: M1 M2 B1 B2;
|