| Specification |
Application: Industrial Ceramic, Alumina Ceramic;
Type: Ceramic Plates;
Useful: Aluminium Filtrate;
Material: Alumina Ceramic;
|
Application: Aerospace, Electronics, Medical, Vacuum Brazing;
Material Composition: Alumina, Al2O3;
Speciality: High Insulation;
Type: Insulating Ceramics;
Compressive Strength: 2300MPa;
Coating Thickness: 8-30μm;
Coating Layer: Mo/Mn;
Plated Layer: Nickel/Copper/Gold etc.;
Thermal Conductivity: 25W/(M.K);
Plating Thickness: 2-9μm;
Max. Use Temperature: 1600ºC;
Density: 3.7g/cm3;
|
Application: Aerospace, Electronics, Medical, Refractory;
Material Composition: Alumina, Al2O3;
Speciality: High Insulation;
Type: Ceramic Part;
Treatment: Glazed, Polishing;
Color: White+Metal;
Coating Thickness: 8-30μm;
Plated Layer: Nickel/Copper/Gold;
Processing Service: Welding, Moulding;
Plating Thickness: 2-9μm;
Max. Use Temperature: 1600ºC;
|
Application: Aerospace, Electronics, Medical, Industrial Ceramic;
Material Composition: Alumina, Al2O3;
Speciality: High Insulation;
Type: Ceramic Parts;
Shape: Customized;
Max Use Temperature: 1600°c;
Color: White;
Compressive Strength: 2300MPa;
Plated Layer: Ni,Cu,Au,etc;
Processing Service: Moulding;
Coaing Thickness: 8-30um;
Flexural Strength: 358MPa;
Coaing Layer: Mo/Mn;
Plating Thickness: 3-9um;
|
Application: Aerospace, Electronics, Medical, Refractory, Industrial Ceramic;
Material Composition: Alumina, Al2O3;
Speciality: High Insulation;
Type: Ceramic Plates;
Flexural Strength: 358MPa;
Shape: Customized;
Plater Layer: Ni,Cu,Au,etc.;
Color: White+Metal;
Max Use Temperature: 1600c;
Compressive Strength: 2300MPa;
Processing Service: Moulding;
Plated Thickness: 2-9um;
Coating Layer: Mo/Mn;
Coating Thickness: 8-30um;
|