Specification |
Al2O3: 40-70%;
Fe2o3: 0.5-2.0%;
Bulk Density: 0.6-1.1 g/cm3;
Product Name: Insulating Brick;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 1-3 MPa;
Classification Temperature: 1200~1600ºC;
Application: Industrial Furnace;
Performance: Excellent;
Grade: Jm23/Jm26/Jm28/Jm30/Jm32;
Thermal Conductivity: Low;
Color: White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35, Sk36, Sk37, Sk38, Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 0.6-1.25;
Cold Crushing Strength: 1.0-10MPa;
Thermal Conductivity: 0.17-0.51;
|
Classification: Clay, Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method, Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 35%~45%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk32-34;
Apparent Porosity: 13-26%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1250-1500;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-3.0%;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, High-Temperature Resistant;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Al2O3: ≥48%;
Apparent Porosity: ≤23%;
|