Specification |
Shape: Conical, Circular, Cylindrical;
Color: White, Light Yellow;
Refractoriness: 1380;
Type: Refractory Material;
Name: Fire Assaying Crucibles;
Working Temperature: 1380;
Item: Ceramic Crucible;
Application: Thermal Analysis or Firing;
Capacity: 10ml, 20ml, 30ml, 50ml, 80ml, 100ml, 200ml, 500ml;
Feature: Long Time Materials, Instant Materials;
Material: Alumina Cement;
Refractoriness (C): 1380;
|
Shape: Round / Oval/Double Thickness;
Color: Brown;
Refractoriness: 1580< Refractoriness< 1770;
Type: Silicon carbide Crucible;
Sample Thickness: 12mm/14mm/15mm;
Paper Tube Inner Diameter: 18mm/37mm/39mm;
Sample Size: Diameter 28mm/30mm/32mm/34mm/37mm;
|
Shape: Boat,High Form,Arc,Columned,Cylindrical,Tray Ect;
Color: White;
Refractoriness: 1770< Refractoriness< 2000;
Type: Ceramic Palette;
Application Domain: Dental,Lab;
|
Shape: Cylindrical;
Color: Ivory;
Refractoriness: Refractoriness> 2000;
Type: Ceramic Parts;
Volume Resistivity (25°c): 3.11X10 ^ 11Ω.Cm;
Water Absorption: 0;
Hardness: Moh's=2;
Thermal Conductivity: 35W/M.K;
Processing Service: Moulding;
Density: 2.15g/cm3;
Compressive Strength: 287MPa;
Micro Hardness (Knoop)(Abside): 691.88 N/mm²;
Maximum Use Temperature: 2200°c;
Flexural Strength: 100MPa;
|
Shape: Round;
Color: White;
Refractoriness: 1770< Refractoriness< 2000;
Type: Crucible;
Bending Strength: >35MPa;
Dielectric Constant: 3.8 - 4.3;
Resistivity: >1012 Ω M;
Oxidizing Atmosphere: 850°c;
Thermal Conductivity: (40-50)W/M K;
Vacuum and Inertia: 2000°c;
Processing Service: Moulding;
Density: 2.25g/cm3;
Compression Strength: >200MPa;
|