Specification |
CAS No.: 25035-69-2'7732-18-5;
Formula: 1000;
Color: White;
Solid Content%: 48-50;
pH: 7-7.5;
PCS: 500-800;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: -/80~~-/85;
Density,g/cm3: 1.20;
Tensile Strength,MPa: 70-95;
Tear Strength,MPa: 200-220;
Elongation at Break,%: 25-150;
Tg,°c: 90-130;
Flexural Strength,MPa: 115-120;
Flexural Modulus,MPa: 2150-2200;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 67-85;
Density,g/cm3: 1.2;
100% Modulus,MPa: 2-5;
300% Modulus,MPa: 4-10;
Tensile Strength,MPa: 20-35;
Tear Strength,MPa: 65-90;
Elongation at Break,%: 600-700;
Tear Strength,Kn/M: 65-90;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 67-85;
Density,g/cm3: 1.2;
100% Modulus,MPa: 2-5;
300% Modulus,MPa: 4-10;
Tensile Strength,MPa: 20-35;
Tear Strength,MPa: 65-90;
Elongation at Break,%: 600-700;
Tear Strength,Kn/M: 65-90;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 67-85;
Density,g/cm3: 1.2;
100% Modulus,MPa: 2-5;
300% Modulus,MPa: 4-10;
Tensile Strength,MPa: 20-35;
Tear Strength,MPa: 65-90;
Elongation at Break,%: 600-700;
Tear Strength,Kn/M: 65-90;
|