Specification |
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance, Volume Stability, Molten Metal Filtration;
Production Process: Unshaped Refractories/Castables;
Refractoriness (℃): Refractoriness<1580;
Shape: Plate;
Type: Refractory Material;
Product Name: Silicon Carbide Ceramic Foam Filter;
Application: Grey Iron/Ductile Iron/Nonferrous Alloy;
Size: 30mm-500mm, Customized;
Filter Shape: Square/Round or Custom;
Material: Silicon Carbide (Sic);
Pore Density: 10/15/20/25/30/40 Ppi (Ppi=Pores Per Inch);
Porosity (%): 80-90;
Operating Temperature: <1500celsius;
Bending Strength (MPa): >0.8;
Compression Strength (MPa): >1.0;
Thermal Sgock Resistance (Times/1100): 6;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate, Board;
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Chemical Composition: Sio2+Cao;
Kind: Reinforcing Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Thermal Shock Resistance, Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Powder, Powder;
Type: Refractory Material;
Material: Al2O3;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance, Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770, 1000ºC;
Shape: Plate, Plate;
Type: Calcium Silicate Boards;
Material: Calcium Silicate;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 230;
Compressive Strength: 0.52-0.6MPa;
Thermal Conductivity: 0.05-0.062W/M.K;
Specification Temp: 1050/650;
Bending Strength: 0.3-0.45;
Sio2: 43%;
Cao: 44%;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Thermal Shock Resistance, Volume Stability, Instant Materials;
Production Process: Semi-Dry Pressing;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Silica Brick, Refractory Material;
Material: Silicon Carbide (Sic);
Sio2: 96%;
Fe2o3: 1.0%;
Ap: 22%;
True Density(g/cm3): 2.34;
CCS: 30MPa;
Rul: 1660c;
|