Specification |
Application: Refractory;
Type: Ceramic Plates;
Product Name: High Porosity Alumina Ceramic Foam Filter for Low-;
Porosity(%): 80-90;
Aperture: 10-50ppi;
Colour: White;
Working Temperature: <1100 Degree;
Bending Strength(MPa): >0.6;
Compression Strength(MPa): >0.8;
Thermal Shock Resistance: 1100degree---Room Temperature 6 Times;
Volume Density: 0.4-0.5g/cm3;
Tolerance of Dimensions: -1.0 / +0 mm (Also Be Customized According to Cus;
Dimension Size: 40-660mm;
Thickness: 11-50mm;
Material: Alumina Ceramic;
|
Application: Aerospace, Brazing, Feedthrough;
Material Composition: Alumina, Al2O3;
Speciality: High Insulation;
Type: Ceramic-to-Metal;
Compressive Strength: 2300MPa;
Mechanical Strength: Excellent;
Color: Metal;
Thermal Conductivity: 25W/(M.K);
Plating Thickness: 2-9μm;
Max. Use Temperature: 1600ºC;
Density: 3.7g/cm3;
|
Application: Aerospace, Industrial Ceramic;
Material Composition: Alumina, Al2O3;
Speciality: High Insulation;
Type: Ceramic Rings;
Shape: Customized Designs;
Size: Size Customized;
Plater Layer: Ni,Cu,Au,etc.;
Processing Service: Moulding;
Advantage: Ideal for High Vacuum Applications;
Product Name: Metallized Ceramic Ring;
Plated Thickness: 2-9um;
Coating Layer: Mo/Mn;
Coating Thickness: 8-30um;
|
Application: Aerospace, Electronics, Medical, Refractory;
Material Composition: Alumina, Al2O3;
Speciality: High Insulation, High Strength;
Type: Ceramic-to-Metal;
Compressive Strength: 2300MPa;
Chemical Resistance: Excellent;
Mechanical Strength: Excellent;
Color: Metal+White;
Thermal Conductivity: 25W/(M.K);
Processing Service: Moulding;
Max. Use Temperature: 1600ºC;
Density: 3.7g/cm3;
|
Application: Aerospace, Electronics, Medical;
Material Composition: Alumina, Al2O3;
Speciality: High Insulation, High Strength;
Type: Insulating Ceramics;
Compressive Strength: 2300MPa;
Coating Thickness: 8-30μm;
Coating Layer: Copper;
Plated Layer: Nickel/Copper/Gold;
Thermal Conductivity: 25W/(M.K);
Plating Thickness: 2-9μm;
Max. Use Temperature: 1600ºC;
Density: 3.7g/cm3;
|