Specification |
Density: 20-270kg/M3;
Hardness Shore C: 20-80;
Tensile: >3MPa;
Elongation: >120%;
Tearing Strength: 260n/M;
Compression Strength: >30+/-10kpa;
Dimensional Change: <3.2%;
Thermal Conductivity: <0.038W/M.K;
Absorbent: <0.04kg/Cm2;
Contraction Percentage: 2.0%~5.0%;
|
Feature: Wear-resistant, Impact-resistant, Heat-resistant, Cold-resistant;
Model No.: EVA Foam.PE Foam;
Advantage: Environmental-Friedly, Nontoxic;
Size: Standard;
Hardness Shore C: 15-35;
Tensile: >3 MPa;
Elongation: >120%;
Tearing Strength: 260n/M;
Compression Strength: >30+/-10kpa;
Dimensional Change: <3.2%;
Thermal Conductivity: <0.038W/M.K;
Absorbent: <0.04kg/Cm2;
Burning Speed: 50 mm/Min;
|
Feature: Wear-resistant, Impact-resistant, Heat-resistant, Cold-resistant;
Model No.: EVA Foam.PE Foam;
Advantage: Environmental-Friedly, Nontoxic;
Size: Standard;
Hardness Shore C: 15-35;
Tensile: >3 MPa;
Elongation: >120%;
Tearing Strength: 260n/M;
Compression Strength: >30+/-10kpa;
Dimensional Change: <3.2%;
Thermal Conductivity: <0.038W/M.K;
Absorbent: <0.04kg/Cm2;
Burning Speed: 50 mm/Min;
|
Feature: Wear-resistant, Impact-resistant, Heat-resistant, Cold-resistant;
Model No.: EVA Foam.PE Foam;
Advantage: Environmental-Friedly, Nontoxic;
Size: Standard;
Hardness Shore C: 15-35;
Tensile: >3 MPa;
Elongation: >120%;
Tearing Strength: 260n/M;
Compression Strength: >30+/-10kpa;
Dimensional Change: <3.2%;
Thermal Conductivity: <0.038W/M.K;
Absorbent: <0.04kg/Cm2;
Burning Speed: 50 mm/Min;
|
Feature: Wear-resistant, Impact-resistant, Heat-resistant, Cold-resistant;
Model No.: EVA Foam.PE Foam;
Advantage: Environmental-Friedly, Nontoxic;
Size: Standard;
Hardness Shore C: 15-35;
Tensile: >3 MPa;
Elongation: >120%;
Tearing Strength: 260n/M;
Compression Strength: >30+/-10kpa;
Dimensional Change: <3.2%;
Thermal Conductivity: <0.038W/M.K;
Absorbent: <0.04kg/Cm2;
Burning Speed: 50 mm/Min;
|