Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Beam;
Material: Silicon Carbide (SiC);
Customization: Yes;
Delivery Time: According to The Detailed Order and Negotation;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: transitional Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.65~2.7g/cm3;
Apparent Porosity: 20 %;
TSR - in water at 1100ºC: 10-15 Cycle;
Refractoriness Under Load: 1650;
CCS MPa: 80-100;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Application Area: Preheating Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.1-2.2g/cm3;
Apparent Porosity: 16%;
Tsr 950ºC: 16cycle;
Rul: 1300;
CCS MPa: 57;
|
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Abrasives, Polishing, Sand Blasting, Grinding;
Shape: Grain, Grit;
Material: Calcined Alumina, Corundom;
Chemical Al2O3: Min: 95%;
Advantage: Manufacturer, Tilting Furnace;
Other Size 1: 12#, 14#, 16#, 20#, 24#, 30#, 36#, 40#, 46#, 54#,;
Other Size 2: 60#, 70#, 80#, 90#, 100#, 120#, 150#, 180#, 220#;
Other Size 3: 0-100 Mesh, 0-200 Mesh, 0-325 Mesh;
Application: Polishing, Blasting, Grinding;
|
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Grain /Grit / Powder;
Material: Alumina Block;
Advantage: Manufacturer, Can Be Customized;
Al2O3: 95% Min;
Fe2o3: 0.3% Max;
Sio2: 1.2% Max;
TiO2: 3.0% Max;
Cao: 0.4% Max;
MGO: 0.4% Max;
Magnetic Particles: 0.05% Max;
Hardness: 9 Mohs;
Specific Gravity: 3.8 g/cm3; Min;
|