Specification |
Application: Aerospace, Electronics, Medical, Refractory, Industrial Ceramic;
Type: Ceramic Parts;
Maximum Use Temperature: 800°c;
Thermal Conductivity (20 °c): 80 - 100 W/M K;
Dielectric Strength (6.35mm): 16.0 - 19.7 AC-Kv/mm;
Volume Resistivity (25°c): 1013 to 1014 ( Ω-Cm );
Fracture Toughness, Kic: 2.75 - 6.0 MPa M1/2;
Flexural Strength, Mor (20 °c): 300 - 460 MPa;
Coefficient of Thermal Expansion: 3.3 - 5.5 1 X 10-6/°c;
Processing Service: Moulding;
Dielectric Loss (Tan): 1 X 10-4 to 5 X 10-4;
|
Application: Aerospace, Electronics, Medical, Refractory;
Type: Ceramic Part;
Material: Hot Pressed Boron Nitride;
Density: 1.5-2.9 g/cm3;
Color: White, Light Grey, Dark Grey;
Thermal Conductivity: 30-85 W/M.K;
Max Working Temperature (in Air): 1000 C;
Max Working Temperature (in Vacuum): 1800 C;
Max Working Temperature (in Inert Gas): 2100 C;
|
Application: Aerospace, Electronics, Medical, Refractory;
Type: Ceramic Part;
Material: Hot Pressed Boron Nitride;
Density: 1.5-2.9 g/cm3;
Color: White, Light Grey, Dark Grey;
Thermal Conductivity: 30-85 W/M.K;
Max Working Temperature (in Air): 1000 C;
Max Working Temperature (in Vacuum): 1800 C;
Max Working Temperature (in Inert Gas): 2100 C;
|
Application: Aerospace, Electronics, Medical, Refractory;
Type: Ceramic Part;
Material: Hot Pressed Boron Nitride;
Density: 1.5-2.9 g/cm3;
Color: White, Light Grey, Dark Grey;
Thermal Conductivity: 30-85 W/M.K;
Max Working Temperature (in Air): 1000 C;
Max Working Temperature (in Vacuum): 1800 C;
Max Working Temperature (in Inert Gas): 2100 C;
|
Application: Aerospace, Electronics, Medical, Refractory;
Type: Ceramic Part;
Material: Hot Pressed Boron Nitride;
Density: 1.5-2.9 g/cm3;
Color: White, Light Grey, Dark Grey;
Thermal Conductivity: 30-85 W/M.K;
Max Working Temperature (in Air): 1000 C;
Max Working Temperature (in Vacuum): 1800 C;
Max Working Temperature (in Inert Gas): 2100 C;
|