Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI, ISO 9001;
Purity: More Than 63%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Melting Point: 1357-1385;
Shape: Wrie, Pipe, Bar, Strip, Plate;
Surface: Bright;
Technique: Cold Treatment;
Manufacturing Process: Solution Treatment;
Tensile Strength: 950 N/mm2;
Yield Strength: 546 N/mm2;
Elogation: 35%;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 70%;
Alloy: Alloy;
Type: Resistance Alloy;
Powder: Not Powder;
The Highest Use Temperature: 1250c;
Resisivity: 1.18;
Density: 8.1g/cm3;
Thickness: 0.1-3mm;
Width: 5-200mm;
OEM: Yes;
Sample: Free;
Surface: Bright or Oxidation;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 70%;
Alloy: Alloy;
Type: Resistance Alloy;
Powder: Not Powder;
The Highest Use Temperature: 1250c;
Resisivity: 1.18;
Density: 8.1g/cm3;
Thickness: 0.1-3mm;
Width: 5-200mm;
Sample: Free;
OEM: Yes;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 70%;
Alloy: Alloy;
Type: Resistance Alloy;
Powder: Not Powder;
The Highest Use Temperature: 1250c;
Resisivity: 1.18;
Density: 8.1g/cm3;
Melting Point: 1380;
Magnetic Properties: Non-Magnetic;
Width: 5-200mm;
Thickness: 0.1-3mm;
Sample: Free;
Surface: Bright;
OEM: Yes;
State: Soft or Hard or Half Hard;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 70%;
Alloy: Alloy;
Type: Resistance Alloy;
Powder: Not Powder;
The Highest Use Temperature: 1250c;
Resisivity: 1.18;
Density: 8.1g/cm3;
OEM: Yes;
Sample: Free;
Surface: Bright;
Thickness: 0.05-2.5mm;
Width: 5-250mm;
Melting Point: 1380;
|