Specification |
Application: Aerospace, Electronics, Medical, Refractory, Industrial Ceramic;
Material Composition: Alumina, Al2O3;
Speciality: High Insulation;
Type: Ceramic Tubes;
Coaing Thickness: 8-30um;
Shape: Customized;
Coaing Layer: Mo/Mn;
Size: Customized;
Color: White+Metal;
Material: 95%Alumina;
Plated Layer: Ni,Cu,Au,etc;
Processing Service: Welding, Moulding, Metallization;
Plating Thickness: 3-9um;
|
Application: Industrial Ceramic, Alumina Ceramic;
Type: Ceramic Plates;
Useful: Aluminium Filtrate;
Material: Alumina Ceramic;
|
Application: Refractory, Medical, Industrial Ceramic, Foundry Molten Metal Filtration;
Type: Ceramic Plates;
Main Material: Zro2;
Color: Yellow;
Working Temperature: up to 1700 Degree C;
Hole Density: 10/20ppi (Ppi=Pores Per Inch);
Porosity(%): 80-87;
Compressive Strength(MPa): 1.5 (Room Temperature);
Bulk Density(g/cm3): 0.9-1.3;
Thermal Shock Resistance: 3times/1350 Degree C to Room Temperature;
Size: 35-200mm;
Material: Zirconia Ceramic;
|
Application: Aerospace, Liquid Metal Filtration;
Type: Ceramic Plates;
Main Material: Zro2;
Color: Yellow;
Working Temperature: up to 1700 Degree C;
Hole Density: 10/20ppi (Ppi=Pores Per Inch);
Porosity(%): 80-87;
Compressive Strength(MPa): 1.5 (Room Temperature);
Bulk Density(g/cm3): 0.9-1.3;
Thermal Shock Resistance: 3times/1350 Degree C to Room Temperature;
Size: 35-200mm;
Material: Zirconia Ceramic;
|
Application: Refractory, Industrial Ceramic, Foundry Molten Metal Filtration;
Type: Ceramic Plates;
Main Material: Zro2;
Color: Yellow;
Working Temperature: up to 1700 Degree C;
Hole Density: 10/20ppi (Ppi=Pores Per Inch);
Porosity(%): 80-87;
Compressive Strength(MPa): 1.5 (Room Temperature);
Bulk Density(g/cm3): 0.9-1.3;
Thermal Shock Resistance: 3times/1350 Degree C to Room Temperature;
Size: 35-200mm;
Material: Zirconia Ceramic;
|